1) modified cellulose wastewater
改性纤维素废水
1.
The application of acid casein air flotation-hydrolytic acidification-contact oxidation process to the treatment of modified cellulose wastewater is presented.
介绍了酸析气浮—水解酸化—接触氧化工艺在处理改性纤维素废水中的应用。
2) modified cellulosic fiber
纤维素纤维改性
3) modified cellulose fiber
改性纤维素纤维
1.
In this paper,using cellulose carbamate (CC) technology,an eco-friendly soybean protein modified cellulose fiber has successfully prepared by the blend spinning of soybean protein solution and cellulose carbamate solution.
采用非粘胶法的纤维素氨基甲酸酯工艺路线,通过大豆蛋白溶液与纤维素氨基甲酸酯溶液共混纺丝,成功地制得了环境友好型大豆蛋白改性纤维素纤维。
4) modified cellulose
改性纤维素
1.
The optimum tanning process of modified cellulose was determined by tanning pickled sheep skins.
通过对浸酸绵羊皮进行鞣制,确定了改性纤维素鞣制最优条件,即鞣剂用量10%、鞣制温度40℃、鞣制初始pH4。
2.
By measuring the Shrinkage Temperature(Ts)and evaluating appearance of leather,the influence of different technological parameters on tanning effect was studied,such as amount of the modified cellulose agent,tanning temperature,pH value and tanning time.
通过对坯革的收缩温度(Ts)和感观的测定,考察了自制的改性纤维素鞣剂的用量、鞣制温度、pH和时间对其鞣制效应的影响,确定了该改性纤维素作为主鞣剂时的最佳应用工艺参数,即:用量25%、温度30℃、鞣制初始pH 4。
6) cellulosic wastewater
含纤维素废水
补充资料：改性纤维
用化学或物理方法使纤维变性而制得的化学纤维。经过物理变性的纤维有异形纤维、变形纤维和复合纤维。用化学方法改性的纤维有接枝纤维、共聚纤维和经化学后处理变性的纤维等。①接枝纤维：在纤维的大分子链上通过活性链节从侧向引上高分子支链所得到的纤维。将棉纤维或粘胶纤维接上甲基、乙基或苯甲基生成纤维素醚，可降低纤维的吸水性并提高纤维的化学稳定性、阻燃性、光作用稳定性、抗热性和电绝缘性等。纤维素与少量能聚合的单体在溶体状态共聚，在纤维素主链上引入合成高分子支链，从而获得接枝共聚的纤维素纤维，可改进纤维素纤维的耐褶皱性。②共聚纤维：由二元或三元单体在一定条件下共聚制得的纤维。丝朊(蛋白质)与少量丙烯腈共聚可获得丙烯腈接枝丝纤维。纯聚丙烯腈纤维的实用价值较差，但经与乙酸乙烯酯和其他单体共聚后所得的纤维，物理机械性质和染色性质就远比纯聚丙烯腈纤维优良。③化学后处理改性纤维:涤纶经1～1.5%萘磺酸碱金属盐和甲醛缩合物水溶液处理可获得抗起球性；而经碱溶液处理，则可具有类似天然丝的性质；在热处理过程中加入含磷或卤素化合物则可获得耐燃性。