1)  Bismuth sulfide
硫化铋
1.
The results show that the well crystallized bismuth sulfide nanorods can be obtained at 160 ℃ under refluxing condition.
采用硝酸铋和硫脲为先驱原料,以离子液为反应介质,合成了硫化铋单晶纳米棒。
2.
Single crystal Bismuth sulfide nanorods were synthesized by refluxing synthetic method, using BiCl3 as bismuth source and CH3CSNH2 as sulfur source,glycol as reaction medium and polyethylene glycol as surfactant.
以三氯化铋(BiCl3)和硫代乙酰胺(CH3CSNH2)为原料,以乙二醇为反应介质,聚乙二醇为表面活性剂,采用回流法合成了硫化铋单晶纳米棒。
3.
Nanostructured bismuth sulfide(Bi2S3) powder samples with different morphologies were synthesized by solvothermal method at 160 ℃ for 120 h using N,N-dimethylformamide(DMF),distilled water and distilled water-ethylene glycol(volume ratio 2:1) as the reaction solvent and Bi(NO3)3·5H2O and L-cystine as the raw materials.
以Bi(NO3)3·5H2O和L-胱氨酸为反应原料,分别以N,N-二甲基甲酰胺(N,N-dimethylformamide,DMF)、蒸馏水-乙二醇(体积比为2:1)和蒸馏水为溶剂,采用溶剂热法在160℃下反应120h,得到了不同形貌的硫化铋(Bi2S3)粉体。
2)  Bi2S3
硫化铋
1.
In this work,bismuth sulfide(Bi2S3)nanorods were successfully fabricated by hydrothermal method.
文章利用水热法在溶液中制备成功硫化铋(Bi2S3)纳米棒。
2.
Bismuth sulfide (Bi2S3) flower-like nanomaterials were synthesized via different surfactants such as Triton X-100+OP-10, TX-10, Triton X-100 by refluxing with bismuth nitrate and thiourea as reactants.
采用硝酸铋和硫脲为反应物,通过添加不同的表面活性剂如TritonX-100+OP-10、TX-10、TritonX-100,用回流法合成了硫化铋纳米花。
3.
The latest development of the preparation of one-dimensional Bi2S3nanopowder is reviewed,including high-temperature solid state synthesis,hydrothemal(solvethermal) synthesis,sonochemical synthesis,microwave-assistant synthesis,and atmospheric boiling and refluxing synthesis.
对一维纳米硫化铋的制备方法如高温固相合成法、水热(溶剂热)法、超声化学法、微波辅助法、常压沸腾回流法等的最新研究进展进行了综述,并对其发展趋势进行了展望。
3)  Bismuth Sulphide
含铋硫化物
1.
The Thermodynamical Analysis of Chloride Leaching Bismuth Sulphide;
含铋硫化物氯盐浸出的热力学分析
4)  bismuthous sulfide
三硫化二铋
5)  bismuth sulfide concentrate
硫化铋精矿
1.
A new process for bismuth sulfide concentrate alkaline smelting at low temperature was presented in this paper to avoiding the shortcomings of the traditional pyrometallurgical process for bismuth extraction, which including high smelting temperature, high energy and material consumption, high production cost and severe environmental pollution.
对主要元素在低温碱性熔炼中的反应进行了热力学分析:计算结果表明硫化铋精矿的低温碱性熔炼反应自还原和碳还原兼可自发进行,碳还原占主导;碳还原反应的可能途径有三种,通过比较每种途径控制步骤的△G~θ发现900K以下途径(二)为主要通过途径,900K以上途径(三)为主要通过途径;计算结果表明AgS、PbS、Cu_2S碱性熔炼条件发生反应生成金属Ag、Pb、Cu;FeS_2、ZnS在碱性熔炼的条件不发生反应进入渣和锍中。
2.
A new process for alkaline smelting bismuth sulfide concentrate into rude bismuth at low temperature was proposed.
提出了硫化铋精矿低温碱性熔炼粗铋的新工艺,考察了w(NaOH)/w(Na2CO3)、碱量、温度和时间等因素对熔炼的影响。
6)  copper bismuth sulphide dregs
铜铋硫化物渣
1.
The catalysis-acid leaching process of copper bismuth sulphide dregs is introduced.
介绍了用催化酸浸工艺从铜铋硫化物渣中回收铜。
补充资料:硫化铋精矿沉淀熔炼


硫化铋精矿沉淀熔炼
precipitation smelting of bismuth concentrate

1 iuhuabi Jingkuang ehendian ronglion硫化秘精矿沉淀熔炼(preeipitation smeltingof bismuth eoneentrate)硫化秘精矿中的硫化秘在冶金炉熔炼高温下与铁屑置换剂反应产出金属秘的过程,为秘冶炼方法之一。秘精矿中的杂质如铅、.锑等硫化物也被置换成金属铅、锑等溶于金属秘中组成粗秘,而杂质铜的硫化物与硫化亚铁反应形成毓。其工艺流程如图。 沉淀熔炼根据硫化秘精矿的成分,除配入适量的铁屑外,还配入纯碱(NaZCO3)、萤石粉(CaF户等熔铁屑硫化锤精矿一 硫化秘精矿沉淀熔炼工艺流程剂,与硫化秘精矿中的脉石成分造渣,为了防止被置换出来的金属秘氧化,在炉料中还需配入少量煤粉作还原剂。 由于硫化秘精矿和配入的熔剂、置换剂、还原剂均为粉料,所以沉淀熔炼可在反射炉、旋转炉、柑祸炉内进行,尤以反射炉最常用。 反射炉熔炼包括配料、进料、升温、熔化、保温沉淀、放渣、放毓、放粗秘、封炉口、清炉等作业,在熔炼的高温阶段炉温要求保持在 1473~1523K之间。为了保护环境和回收有价金属,出炉烟气要经过袋滤器收尘处理。沉淀熔炼反应的产物粗秘、梳和炉渣在炉内高温下因其密度差异而分层,经6h以上沉淀分离即可分别放出。产出的粗钮尚需进一步精炼为精秘。 沉淀熔炼的硫化秘精矿平均含秘约20%~25%,含硫在20%左右;因此配料中必须加入大量铁屑,所产出的铣量大,铣以硫化亚铁为主,一般为粗秘量的2.5一4倍。这种贫铣的处理较困难,经济效益不好,但不处理又影响其中银、铜、秘等有价金属的回收。所以·机淀熔炼已逐渐被含秘物料混合熔炼所取代。