2) Magnesia-zirconia products
镁锆制品
3) magnesite product
菱镁制品
1.
Exploration on the problems of properties and application of magnesite product;
菱镁制品的性能及使用问题探讨
2.
This paper analyzes the essential scumming reasons for magnesite product and every kind of modified measures and results used normally now.
分析了菱镁制品返卤泛霜的根本原因及目前常用的各种改性措施及效果 ;在此基础上 ,通过添加多种新型混合活性改性剂及新的处理方法的试验研究 ,使菱镁制品返卤泛霜现象得到明显的抑
4) Mg-Al product
镁铝制品
5) calcium magnesia carbon products
镁钙碳制品
1.
The oxidation-resistance ability of calcium magnesia carbon products has been increased 20～ 30% after light burning them at 800℃ for 3 hours and oil-soaking at vaccum.
镁钙碳制品采用800℃×3h 轻烧,真空油浸工艺后,抗氧化能力提高20%～30%,炭化处理后的耐压强度提高约40%,气孔率明显降低,抗水化能力、常温耐压强度、体积密度显著提高。
6) magnesium oxychloride cement product
氯氧镁水泥制品
1.
Based on this, the performance of magnesium oxychloride cement product with high content is studied by the uniform test.
通过对比试验研究了不同掺灰量对氯氧镁水泥强度和耐水性的影响,得出粉煤灰最佳掺量;在此基础上,采用均匀试验研究了大掺量粉煤灰氯氧镁水泥制品的性能。
2.
The cause of the active magnesia of magnesium oxychloride cement products and the effect of various common methods at present of the property modification is analysed,the essential measures to solve the active magnesia of magnesium oxychloride cement products is advanced.
通过试验分析了氯氧镁水泥制品返卤泛霜的原因及目前常用的各种改性措施的效果，并找到从根本上解决氯氧镁水泥制品返卤泛霜的方法。
补充资料：电熔镁铬质耐火制品
分子式：
CAS号：
性质：又称电熔镁铬质耐火制品。以电熔法制成的镁铬质耐火材料。其矿物组成主要有方镁石和尖晶石。主要化学成分是氧化镁为50%～60%，氧化铬为15～20%，氧化铝为10%～15%。氧化铁为10%～15%。体积密度为3.3～3.4g/cm3，显气孔率为5%～15%，常温强度和高温强度比普通镁铬砖高得多，并具有耐磨性高和抗渣性强等优点。但抗震性能较差。以镁砂、铬矿和高铝矾土（或工业氧化铝）为原料，经粉碎、配料制成素坯，置于电弧炉中高温熔化，熔融液注入模中，经慢冷退火而制成。主要用于炼铜闪速炉、炼钢电炉的过热部位和炉顶、转炉易损部位、真空处理炉内衬等。
CAS号：
性质：又称电熔镁铬质耐火制品。以电熔法制成的镁铬质耐火材料。其矿物组成主要有方镁石和尖晶石。主要化学成分是氧化镁为50%～60%，氧化铬为15～20%，氧化铝为10%～15%。氧化铁为10%～15%。体积密度为3.3～3.4g/cm3，显气孔率为5%～15%，常温强度和高温强度比普通镁铬砖高得多，并具有耐磨性高和抗渣性强等优点。但抗震性能较差。以镁砂、铬矿和高铝矾土（或工业氧化铝）为原料，经粉碎、配料制成素坯，置于电弧炉中高温熔化，熔融液注入模中，经慢冷退火而制成。主要用于炼铜闪速炉、炼钢电炉的过热部位和炉顶、转炉易损部位、真空处理炉内衬等。