1) Spinel lithium ion-sieve
尖晶石锂离子筛
2) lithium ion-sieve
锂离子筛
1.
Synthesis and properties characterization of spinel-type lithium ion-sieve precursor;
尖晶石型锂离子筛前驱体的制备和性能表征
2.
The exchange performance of the lithium ion-sieve is studied,which was synthesized with LiOH and reduction-ammoniacal leaching residue of polymetallic nodules.
针对以LiOH和多金属结核还原氨浸渣为原料合成的正尖晶石结构的锂离子筛的吸附性能展开研究。
3) lithium ion sieve
锂离子筛
1.
6O4 of lithium ion sieve was prepared with a selective starting reagents MnCl2·4H2O and LiOH·H2O by soft chemistry route such as sol-gel, hydrothermal and heat treatment.
以MnCl2·4H2O,LiOH·H2O等试剂为初始原料,采用溶胶-凝胶、水热处理、固化等软化学合成步骤制备了锂离子筛前驱体Li1。
4) Li-Mn spinel
锂锰尖晶石
5) Li-Al-O spinel
锂铝尖晶石
1.
The Li-Al-O spinel support was synthesized by impregnation of γ-Al2O3(2-3 mm) with aqueous LiNO3 solution.
采用Li NO3对γ-Al2O3进行改性,制备了以多孔锂铝尖晶石为载体,以Pd为活性组分的PdCl2-CuCl2/Li-Al-O负载型催化剂,并考察了催化剂对CO低压气相合成碳酸二乙酯(DEC)反应的催化性能,探讨了载体Li/Al比、改性浸渍方法、不同改性金属、Pd负载量和反应压力等因素对催化剂催化性能的影响。
6) inverse spinel ions
反尖晶石离子
1.
Effects of inverse spinel ions(Fe3+ ,Ga3+ ,Al3+ ) doping on structure and electrochemical performance of positive electrode materials of lithium manganese oxide were researched.
阐述了锂离子电池锰酸锂正极材料掺杂的重要性,研究了反尖晶石离子掺杂(Fe3+、Ga3+、Al3+)对锰酸锂正极材料结构和电化学性能的影响,并提出了影响锂离子电池充放电循环性能的机理。
补充资料：尖晶石
| 尖晶石 spinel 镁铝的氧化物矿物（MgAl2O4）。 化学成分中类质同象替代很普遍，常可含铁、锌、铬、锰等。等轴晶系，晶体常呈八面体和八面体与菱形十二面体的聚形。以八面体面为双晶面和接合面构成尖晶石律双晶。无色，含色素离子时可呈红、蓝、绿、褐、黄等色。玻璃光泽。莫氏硬度8，比重3.55。由接触交代作用或结晶于基性、超基性火成岩中，透明而色泽艳丽者是高档宝石材料。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。