1) Sensitization
[英][,sensitai'zeiʃən] [美][,sɛnsətə'zeʃən]
敏化
1.
Research on Sensitization Methods of Emulsion Explosives;
乳化炸药敏化方法的研究
2.
Study on the sensitization of the powder composition of Non-TNT ammonium nitrate explosive;
无梯粉状硝铵炸药的敏化研究
2) sensitizing
[英]['sensi,taiz] [美]['sɛnsə,taɪz]
敏化
1.
Study on TiO_2 films sensitizing and its bactericidal activity;
TiO_2膜的光敏化及其灭菌活性研究
2.
The optimal process conditions were determined: roughening for 6 min at 55～65 ℃,sensitizing and activating for 3～4 min at ambient temperature,electroless nickel plating for 10 min at 40～50 ℃.
研究了常温下敏化活化一步进行的ABS塑料化学镀镍工艺。
3.
As the sensitizing temperature(550 - 650 ℃) of the 316 S.
研究表明:316不锈钢在此环境下,由于敏化所造成的晶间腐蚀不可避免,而316Ti和316L不锈钢的抗晶间腐蚀性能优于316不锈钢。
3) sensitize
[英]['sensətaɪz] [美]['sɛnsə'taɪz]
敏化
1.
Photoelectrochemical Studies on Dye sensitized ZnO Ultra Particle Film;
染料敏化后ZnO超微薄膜的光电性能
2.
Research development of the dye sensitized solar cell;
染料敏化纳米薄膜太阳电池的研究进展
3.
Mainly,it talked about the effect of concentration sensitize solution and activation solution to electroless process.
着重研究了敏化浓度和活化浓度对化学镀的影响,以及研究不同pH值对化学镀层含磷量的影响。
4) sensitized
[英]['sensi,taiz] [美]['sɛnsə,taɪz]
敏化
1.
Review on sensitized TiO_2 nanocrystalline solar cell;
敏化纳米晶TiO_2太阳电池
2.
The results show that the microstructure near the welding heat affective zone is sensitized due to the welding process.
分析结果表明,材料焊接热影响区的敏化效应、管内介质的腐蚀作用以及弯管振打块附近的应力集中导致该管发生了晶间应力腐蚀开裂。
3.
The structure and operation of sensitized TiO2 nanocrystalline solar cells were introduced.
介绍了敏化TiO2纳米晶太阳能电池的工作原理和表征方法，并对常用的制备工艺、敏化剂的选择、目前达到的水平进行了综述，在此基础上提出了一些值得深入研究的问题。
5) sensibilization
敏化
1.
On the basis of the expatiation of the stainless steel's sensibilization and intergranular corrosion theory,the process and ca.
在系统阐述了不锈钢敏化及晶间腐蚀理论的基础上,详细分析了410S产生晶间腐蚀的过程及原因,并简要探讨了大生产中控制该缺陷的可行措施。
2.
It points out that the sensibilization of ZnS concentrate is specially important.
研究了浸出中的技术问题,指出硫化锌精矿的敏化对锰的提取尤为重要。
6) sensitization and activation
敏化活化
1.
The results showed that the bonding force between the film and the substrate is better after the substrate dealed with the pretreatment of sensitization and activation compared to that without pretreatment.
结果表明:与基体的前处理中无敏化活化相比,对基体沉积前采用敏化活化前处理得到的薄膜与基体的结合力强,薄膜起皮现象少;稀土镧大幅度提高了薄膜的沉积速度,稀土铈增加了薄膜的光亮性,很大程度地提高了薄膜表面质量;不管基体是否敏化活化,镧和铈均提高了镀液的稳定性。
补充资料：敏化
分子式：
CAS号：
性质： 不锈钢在450～800℃温度区间停留一段时间或缓慢冷却，从而导致晶界析出以Cr23C6为主的铬的碳化物的过程。敏化使晶界附近区域的铬含量降低，耐蚀性下降，在使用过程中发生晶间腐蚀的敏感性增大。
CAS号：
性质： 不锈钢在450～800℃温度区间停留一段时间或缓慢冷却，从而导致晶界析出以Cr23C6为主的铬的碳化物的过程。敏化使晶界附近区域的铬含量降低，耐蚀性下降，在使用过程中发生晶间腐蚀的敏感性增大。