1) glass forming region
成玻区
1.
The complete glass forming region has been obtained by XRD analysis.
针对Na2O-TeO2-WO3体系碲钨酸盐玻璃进行了研究,绘制了该体系完整的成玻区,利用DSC和Raman测试分析了该系玻璃的热稳定性及结构。
2) glass-forming region
玻璃形成区
1.
Study on glass-forming regions and performance of CaO-SiO_2-B_2O_3 system
CaO-B_2O_3-SiO_2系玻璃形成区及性能研究
2.
Glass-forming range of samarium borosilicate glasses was explored by the experiments of glass-forming region.
通过玻璃形成区实验探索了含钐稀土硼硅酸盐玻璃的形成区范围,研究了Sm2O3含量对稀土玻璃形成区的影响和相应的玻璃形成区图,以及Al2O3含量对含钐稀土硼硅酸盐玻璃形成区的影响。
3.
A new series of chalcohalide glasses in GeSe2-Ga2Se3-KBr system were prepared and the glass-forming region was determined.
制备了GeSe2-Ga2Se3-KBr体系的硫卤玻璃,运用差热分析(DTA)、密度测试、X射线衍射(XRD)、紫外-可见光谱(UV-Vis)和红外光谱(IR)等各种分析测试方法,确定了该体系玻璃的玻璃形成区系统并研究了GeSe2-Ga2Se2-KBr硫卤玻璃的成玻能力和光学性能。
3) glass formation region
玻璃形成区
1.
The method of conversional melting glass are used to study the glass formation regions of Bi2O3-B2O3-TiO2-RmOn quaternion systems (RmOn is La2O3.
采用传统的玻璃熔融方法,研究了Bi2O3-B2O3-TiO2-RmOn四元系统的玻璃形成区(RmOn分别为La2O3、 Sb2O3、ZrO2、SiO2和Nb2O5氧化物),给出了上述四元系统的玻璃形成范围。
4) prediction of glass forming region
玻璃形成区预测
5) region of binary glass formation
二元玻璃生成区
6) region of ternary glass formation
三元玻璃生成区