1) sinter-HIP(SH)
烧结-热等静压(SH)
2) Sinter-HIP furnace
烧结-热等静压炉
1.
Optimization of cemented carbide sinter-HIP furnace;
硬质合金烧结-热等静压炉的优化
2.
Improving the distribution of temperature field in Sinter-HIP furnace graphite canister by the optimum design of graphite heaters,to solve the problem about the uneven distribution of temperature field in graphite canister and the temperature of the bottom and the space near the graphite canister's door in the graphite canister are relatively lower.
通过对烧结-热等静压炉石墨发热体的优化设计,改善石墨筒内温度场的均匀性,以解决实际生产中存在的石墨筒内温度分布不均匀、底部空间和靠近两个炉门侧空间温度偏低的问题,并对石墨发热体改进前后石墨筒内温度场分布情况进行了数值仿真。
3) sintering-HIP
烧结-热等静压
1.
Coarse-grain WC-15Co,WC-22Co and micro grin WC-12Co-1Cr_3C_2,medium-grain WC-12Co cemented Carbide were made by sintering and HIP and sintering-HIP.
应用烧结加热等静压和烧结-热等静压两种工艺制备了粗晶WC-15Co、WC-22Co和微晶WC-12Co-1Cr3C2、中等晶粒WC-12Co硬质合金,从原理、经济性论述了这两种工艺的差异及其对WC-Co硬质合金组织和性能的影响。
4) hot isostatic pressing sintering
热等静压烧结
1.
Microstructural study on Nd-Fe-B permanent magnets prepared by hot isostatic pressing sintering;
热等静压烧结Nd-Fe-B永磁体
5) isostatic sintering
等静压烧结
6) vacuum sinter/HIP
真空烧结/热等静压
补充资料：热等静压
在高温下利用各向均等的静压力进行压制的工艺方法。在发动机制造中，热等静压机已用于粉末高温合金涡轮盘和压气盘的成型。把高温合金粉末装入抽真空的薄壁成形包套中，焊封后进行热等静压，除去包套即可获得致密的、接近所需形状的盘件。粉末热等静压材料一般具有均匀的细晶粒组织,能避免铸锭的宏观偏析,提高材料的工艺性能和机械性能。粉末高温合金热等静压或热等静压加锻造的盘件已在多种高推重比航空发动机上应用。同样，热等静压还用于制造粉末钛合金风扇盘和飞机上的粉末铝合金和粉末钛合金承力构件。在航天器制造工业中，热等静压主要用于制造致密的碳质结构件，如火箭的舵面和固体火箭发动机喷管喉衬等。
各种合金的精密铸件，如高温合金涡轮叶片和铸钛机匣等，经热等静压致密化处理可消除内部疏松和缩孔，提高性能、可靠性和使用寿命。热等静压还是返修旧件以延长使用寿命的一种有效方法。
大多数生产型热等静压机的最高使用温度约1400°C，最大压力在100～200兆帕(1000～2000大气压)之间。现代最大的热等静压机的总吨位约 40万千牛（4万吨力）。
各种合金的精密铸件，如高温合金涡轮叶片和铸钛机匣等，经热等静压致密化处理可消除内部疏松和缩孔，提高性能、可靠性和使用寿命。热等静压还是返修旧件以延长使用寿命的一种有效方法。
大多数生产型热等静压机的最高使用温度约1400°C，最大压力在100～200兆帕(1000～2000大气压)之间。现代最大的热等静压机的总吨位约 40万千牛（4万吨力）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。