1) asbestos tailings
石棉尾矿
1.
Effect of pre-treatment of asbestos tailings on acid leaching reaction of asbestos tailings;
预处理对石棉尾矿酸浸反应效果的影响
2.
The best technology parameters are studied in the production of precipitated silicon dioxide,light magne sium oxide and by-products of sodium sulfate and iron oxide red from the asbestos tailings in a wet method.
探讨了以石棉尾矿为原料，采用湿法生产沉淀二氧化硅和轻质氧化镁，副产硫酸钠、氧化铁红等化工原料的最佳工艺参数，充分利用了陕西省的矿产资源，解决了石棉尾矿的环境污染问题。
3.
The optimal technical condition of the preparation of amorphous silica by purifying acid leaching residues of asbestos tailings was reported.
对提纯石棉尾矿酸浸渣制备无定型二氧化硅的最优工艺条件进行研究。
2) asbestos tailing
石棉尾矿
1.
Application research of asbestos tailing in highway concrete
石棉尾矿在道路混凝土中的应用研究
2.
The acid leaching residue of asbestos tailing was pretreated by calcination.
采用煅烧方法对石棉尾矿酸浸渣进行预处理,通过比表面积测定仪对煅烧前后的酸浸渣进行了表征,研究了煅烧后的石棉尾矿酸浸渣对溶液中Cr3+的吸附性能,并对吸附机理进行了探讨。
3.
This text introduced the pollution status of asbestos tailing during asbestos exploitation,and analysed the speciality of asbestos tailing and its advancement of utilization as resource.
本文介绍了石棉矿开采过程中排放的石棉尾矿污染现状,分析了石棉尾矿特点及其资源化利用研究进展。
3) acid leaching residue of asbestos tailing
石棉尾矿酸浸渣
1.
After processed,acid leaching residue of asbestos tailing with the high amorphous SiO2 and the huge surface area could be made as the artificial silicon fume(ASF).
石棉尾矿酸浸渣具有较高的无定形SiO2含量和巨大的比表面积,对其处理加工后可制得人造硅灰,本文通过水泥胶砂强度、标准稠度用水量、凝结时间和水泥净浆流动度试验,对人造硅灰的制备工艺及应用性能进行了初步研究。
2.
The acid leaching residue of asbestos tailing was pretreated by calcination, and the adsorption capability of calcined acid leaching residue of asbestos tailing to Cu2+ was studied.
对石棉尾矿酸浸渣进行了焙烧处理,考察了焙烧后的石棉尾矿酸浸渣对溶液中Cu2+的吸附性能,测定了其表面ξ电位,对吸附Cu2+前后的石棉尾矿酸浸渣进行了表征,探讨了吸附机理。
4) the Asbestos Mine
石棉矿
1.
The Analysis of Sinkholes Geological Hazards Treatment Take the Asbestos Mine of Dalian E&T Development Zoon as an Example;
地质灾害治理及费用分析——以大连开发区石棉矿为例
5) asbestos deposit
石棉矿床
6) rock wool
矿石棉
补充资料：石棉
| 石棉 asbestos 能劈分成细长而柔韧纤维的硅酸盐矿物的统称。通常只作为具有上述特性的纤蛇纹石和闪石的某些纤维状变种的统称。按成分和内部结构可分为蛇纹石石棉（温石棉）和闪石石棉两类。闪石石棉又分为直闪石石棉（铁石棉）、透闪石石棉和阳起石石棉（狭义的石棉）、蓝石棉（钠石棉）3种。在研钵中研磨，蛇纹石石棉成混乱的毡团，纤维不易分开；而闪石石棉则分散成许多细小的纤维。不含铁的石棉呈白色，含铁的呈不同色调的蓝色。石棉未劈分前的纤维状集合体显丝绢光泽，劈分后的纤维光泽暗淡。石棉还具有耐酸、耐碱、耐高温和绝缘等性能，蛇纹石石棉的柔韧性、抗拉强度、电绝缘性和耐高温能力强于闪石石棉，而在耐酸、耐碱和防腐蚀能力方面闪石石棉则优于蛇纹石石棉。石棉被广泛用于传动、保温和绝缘装置中。纤维长度超过8毫米的石棉与20％～25％的棉纱混合可制成防火纺织材料，较短的纤维可用于制作石棉胶合布、石棉板和绝缘材料等。蓝石棉具有独特的防化学毒物和净化放射性微粒污染空气的性能，被用于制作各种高效能过滤器。蛇纹石石棉分布广，占石棉总产量的95％。它主要形成于侵入体与白云岩或白云质灰岩的接触带和超基性岩经变质作用形成的蛇纹岩的网状裂隙中。闪石石棉多在动力变质条件下，由热液提供钠、镁质交代含铁硅质岩而成。 |