1) mesoporous carbon
中孔碳
1.
The presence of Ni was crucial to the formation of graphitized mesoporous carbon.
结果发现,通过Ni的催化作用,可在较低温度下得到高度石墨化的中孔碳材料。
2.
Mesoporous carbons(MCs)were prepared by an imprinting method,using mesophase pitch and nanometer colloidal silica solution as carbon precursors and pore generators,respectively.
用中间相沥青作碳源,硅胶水溶液作造孔剂,采用胶体印刻法制得一系列中孔碳。
2) CMK-5 mesoporous carbon
CMK-5中孔碳
3) Mesoporous titanium carbides
中孔碳化钛
1.
Mesoporous titanium carbides were prepared via carbothermal reduction of organic-inorganic gels using titanium n-butoxide as a Ti source and sucrose as a carbon precursor.
以钛酸正丁酯为钛源、蔗糖为炭源,采用溶胶-凝胶法制得有机-无机复合干凝胶,后经高温炭热反应、氯气化学刻蚀分别得到中孔碳化钛及碳化物基炭材料(CDCs)。
4) mesopore activated carbon fiber
中孔活性碳纤维
1.
In recent years more uses have been found for this material with the advent of mesopore activated carbon fiber.
近年来,中孔活性碳纤维的研究拓宽了其应用领域。
5) hollow-porous carbon fibers
中空多孔碳纤维
1.
These materials consist of two-layers,one made of PAN-derived hollow-porous carbon fibers contributing to the low density,and the other made of carbon blacks,short carbon fibers or carbonyl iron powders acting as the matching layer.
以羰基铁粉作吸收剂的匹配层比以炭黑和碳纤维作吸收剂的匹配层对提高以中空多孔碳纤维吸波材料的吸波性能更为显著。
6) perforated carbon steel base
带孔的碳钢中心管
补充资料：多孔碳晶须
分子式：
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。