1) fine lamellar pearlite
细片状珠光体
2) lamellar pearlite
片状珠光体
1.
It is a question worth discussion whether lamellar pearlite and sorbite could co-exist in the view field of optical microscopes and whether lamellar pearlite and sorbite could be identified simply via lamellar structures.
在光学显微镜的视场中,片状珠光体与索氏体是否可以共存;同时,是否可以简单地根据是否能够区分层片状结构来划分片状珠光体与索氏体值得探讨。
2.
45 steel row material for cold extrusion performed pre-normalizing can eliminate the widmannstaetten structure,banded structure,and form the uniform lamellar pearlite.
45钢冷挤压零件原材料预先正火,彻底消除魏氏组织、带状组织,形成均匀片状珠光体,然后在球化退火时,才能获得碳化物颗粒均匀、圆整、弥散分布在铁素体基体上的理想组织。
3) big flake perlite
粗片状珠光体
1.
Results show that large quantities of big flake perlite occurring in the structure of the wire rod is the cause directly to the rupture of the wire rod.
大量粗片状珠光体的形成与吐丝前后的冷却速度过慢等因素有关。
4) nodular fine pearite
球状细珠光体
5) sphere pearlite(granule)
球状珠光体(细粒状)
6) nodular troostite
团状屈氏体;细珠光体
补充资料：珠光体
奥氏体在A1温度共析分解产生的组织，本质上是一种铁素体和渗碳体相间成层排列的混合物。由于显微镜下图象状似珠母，被称为pearlite，译名珠光体。珠光体是钢中最常见的组织之一。珠光体一词又常用于描述冶金学中所有其他成层排列的共析组织(见铁碳平衡图)。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。