1) nano-sized magnesium hydroxide
纳米氢氧化镁
1.
Study on new preparation technology of nano-sized magnesium hydroxide by lime-brine method;
卤水-石灰乳法制备纳米氢氧化镁新工艺研究
2.
Research on preparation technology of high purity nano-sized magnesium hydroxide by impinging stream;
撞击流制备高纯纳米氢氧化镁技术研究
3.
Preparation of nano-sized magnesium hydroxide as a flame retardant by high gravity technology and its application;
超重力技术制备纳米氢氧化镁阻燃剂的应用研究
2) nanometer magnesium hydroxide
纳米氢氧化镁
1.
Experimental study on drying kinetics of nanometer magnesium hydroxide;
纳米氢氧化镁的干燥动力学试验研究
2.
Preparation and applications of nanometer magnesium hydroxide;
纳米氢氧化镁材料的制备与应用
3.
The investigation on nanometer magnesium hydroxide as a flame retardant has been drawn increasing attentions recently.
近年来纳米氢氧化镁阻燃剂越来越受到人们的关注。
3) nano-magnesium hydroxide
纳米氢氧化镁
1.
Properties of nano-magnesium hydroxide/rubber composite;
纳米氢氧化镁/橡胶复合材料的性能研究
2.
The effect of nano-magnesium hydroxide on the reinforcement property,the flame resistance,the blending ratios of SBR/NR and the blend mechanical property was studied in this paper.
研究了纳米氢氧化镁对丁苯橡胶(SBR)/天然橡胶(NR)并用胶的补强性能、阻燃性能及SBR/NR并用比对胶料力学性能的影响。
4) nano-Mg(OH)_2
纳米氢氧化镁
1.
Preparation of Highly Dispersed Nano-Mg(OH)_2 Via Double Injection-Hydrothermal Method;
双注—水热法制备高分散纳米氢氧化镁的工艺研究
2.
The high flame retardant polyurethane(HFPUR) elastomer was prepared by high reactive flame retardant polyether polyol(HIROL) and toluene diisocyanate,which was compounded with nano-Mg(OH)_2/dimethyl methyl phosphite(DMMP).
将纳米氢氧化镁浸润甲基膦酸二甲酯(DMMP)作为填料,共混入由含溴阻燃聚醚多元醇(HIROL)和甲苯二异氰酸酯(TDI)制得的阻燃聚氨酯预聚物(FPUR)中,制成高阻燃聚氨酯弹性体(HF PUR)。
5) magnesium hydroxide nanorods
氢氧化镁纳米棒
1.
A Study on the Characteristics of Drying Kinetics of Magnesium Hydroxide Nanorods
氢氧化镁纳米棒的干燥动力学特性研究
2.
Basic magnesium chloride nanorods are prepared with MgCl2 and light MgO by liquid phase method,and then magnesium hydroxide nanorods with a diameter range of 100-150 nm and average length of 3-5μm are synthesized with basic magnesium chlorides nanorods as precursor by precipitate transformation method.
以氯化镁和轻质氧化镁为原料,采用液相法制备出碱式氯化镁纳米棒;再以碱式氯化镁纳米棒为前驱物,经沉淀转化法合成出直径约100~150 nm,长约3~5μm的氢氧化镁纳米棒。
6) nano magnesium hydroxide
纳米氢氧化镁(NMH)
补充资料：氢氧化镁阻燃剂
氢氧化镁阻燃剂
其阻燃机理如下：氢氧化镁在受热时（340-490度）发生分解吸收燃烧物表面热量起到阻燃作用；同时释放出大量水分稀释燃物表面的氧气，分解生成的活性氧化镁附着于可燃物表面又进一步阻止了燃烧的进行。氢氧化镁在整个阻燃过程中不但没有任何有害物质产生，而且其分解的产物在阻燃的同时还能够大量吸收橡胶、塑料等高分子燃烧所产生的有害气体和烟雾，活性氧化镁不断吸收未完全燃烧的熔化残留物，从使燃烧很快停止的同时消除烟雾、阻止熔滴，是一种新兴的环保型无机阻燃剂。
阻燃剂按化学成份可以分为有机阻燃剂和无机阻燃两大类。有机阻燃剂又分为磷系和卤系两个系列。由于有机阻燃剂存在着分解产物毒性大、烟雾大等缺点，正逐步被无机阻燃剂所替代。
无机阻燃剂主要品种有氢氧化铝、氢氧化镁、红磷、氧化锑、氧化锡、氧化钼、钼酸铵、硼酸锌等，其中以氢氧化铝和氢氧化镁因分解吸热量大，并产生h2o可起到隔绝空气作用，其分解后氧化物又是耐高温物质，故二种阻燃剂不仅可起到阻燃作用，而且可以起到填充作用，它所具有不产生腐蚀性卤气及有害气体、不挥发、效果持久、无毒、无烟、不滴等特点。
目前国内氢氧化铝用量较多，但随着高聚物加工温度的提高，氢氧化铝易分解，降低阻燃作用，氢氧化镁较氢氧化铝具有如下优点：
①氢氧化镁热分解温度达330℃，比氢氧化铝高100℃，故有利于塑料加工温度的提高，加快挤塑速度，缩短模塑时间；
②氢氧化镁与酸的中和能力强，可较快地中和塑料燃烧过程产生的酸性气体so2、nox、co2等；
③氢氧化镁分解能高，有利于吸收燃烧热，提高阻燃效率；
④氢氧化镁抑烟能力强、硬度小，对设备摩擦小，有助于延长生产设备寿命