1) melt phase-separation
熔融分相法
1.
Nanometer TiO_2 photocatalytic material was prepared by melt phase-separation,the samples of TiO_2 were characterized with XRD,SEM,TEM and testing of photocatalytic capability were made using sewerage being a degradation material.
利用熔融分相法制备了纳米TiO_2光催化村料,用XRD,SEM,TEM技术对其结构进行了表征,并进行了光催化降解污水的实验。
2.
Nanometer TiO2 photocatalytic material was prepared by melt phase-separation.
实验采用了熔融分相法制备纳米TiO_2光催化材料,本文研究了该制备方法的实验原理,采用D T A,X R D,SEM,TEM等测试手段对实验结果进行分析,并对不同条件下热处理样品的T iO_2晶体的析晶情况进行讨论,用甲基橙作为模拟降解物进行光催化性能的测试。
2) melt-phase separation
熔融-分相
3) decomposition by fusion
熔融分解法
4) hot dispersion-ultrasonic technique
熔融超声分散法
1.
Method: To prepare solid lipid nanoparticles(SLN) loaded with Xionggui powder-supercritical carbon dioxide fluid extraction(XG-CO_2-SFE) using a hot dispersion-ultrasonic technique,establishing the best prescription of XG-CO_2-SFE-SLN through orthogonal design methods using entrapment efficiency of nanoparticles as index,and investig.
方法:采用熔融超声分散法制备芎归散超临界CO2萃取物固体脂质纳米粒混悬液,以包封率为考察指标,采用正交试验筛选最佳处方,并考察其物理化学性质;采用动态透析法考察其在不同介质中的释药特性。
6) solid phase fusion
固相熔融
补充资料：分相
分相
phase separation
fenxiang分相(phase separation)硅酸盐熔体和玻璃中某些组分在一些区域内偏聚形成化学组成不同相的现象.20世纪90年代以来用电镜对二、三组分和多组分玻瑞进行的研究表明，所有玻璃都有微不均区(分相)，例如AI:03一510:系在A120:含量10%~50%范围，在小于1600℃存在着分相区域，这对耐火纤维使用中的变化有重要意义。分相的根本原因是热力学自由烤的降低，其机理有成核生长与不稳分解两种，前者组成变化大，但是空间分布范围小;后者组成变化小而空间弥散范围大。分相造成亚微结构不均匀。 (李晓明)