1) mechanical plating
机械镀
1.
The properties of mechanical plating of zinc and zinc-aluminum;
机械镀锌及锌铝复合镀层性能研究
2.
Effect of rare earth on formation and property of coating deposited by mechanical plating without crystallizing;
稀土对机械镀无结晶形成过程及镀层性能的影响
3.
Zinc based RE alloy coating was obtained on the surface of steel samples by adding RE metal salts during the mechanical plating process.
通过在机械镀锌过程中添加不同量的稀土金属盐,在钢铁试样表面形成不同成分含量的锌基稀土合金镀层。
2) mechanical plated coating
机械镀镀层
1.
Three kinds of mechanical plated coatings were formed with 325 or 800 mesh spherical zinc powder and zinc-aluminum compound flakes from ball-milled and 325 mesh spherical zinc-aluminum mixed powder(10% Al).
为研究机械镀镀层性能与原料粉之间的关系,采用325,800目球形颗粒状锌粉和325目球状锌-10%(质量分数)铝粉混合球磨成的片状锌-铝复合粉制成3种机械镀镀层,考察了金属原料粉及形成镀层的SEM形貌。
3) mechanical plating
机械镀锌
1.
Choosing of impact media for mechanical plating;
机械镀锌冲击介质的选择
2.
Mechanism of mechanical deposition in mechanical plating;
机械镀锌沉积机理的研究
4) mechanical zinc plating
机械镀锌
1.
The production process of mechanical zinc plating on hinge;
铰链机械镀锌的生产工艺
2.
Cause analysis of zinc ball production in mechanical zinc plating;
机械镀锌过程锌球产生的原因分析
3.
The process of surface treatment of cast iron hardware and the process flows of its mechanical zinc plating were introduced.
介绍了铸铁五金件的表面处理工艺及其机械镀锌工艺流程。
5) mechanical zincification
机械镀Zn
1.
The surface Zn coating by mechanical zincification technology was suaessfully applied for highway guardrail bolt.
高速公路护栏螺栓采用机械镀Zn的表面处理工艺 ,与热浸镀相比具有保证质量、镀层厚度可按要求任意控制、耐腐蚀性能好、生产效率高、成本低、后处理简单等优
6) mechanical galvanizing
机械镀锌
1.
Assessment of adhesion strength of mechanical galvanizing coating by pull-off test method;
拉开测试法评定机械镀锌层的结合强度
2.
The corrosion resistance of two different zinc layers of mechanical galvanizing is discussed through salt spray test.
通过盐雾腐蚀试验比较讨论两种不同的机械镀锌层的耐蚀性,得到了一种耐蚀性好的机械镀锌工艺,对获得高防护机械镀锌层的工艺研究有参考价值。
3.
On the basis of environmental protection,the harmful origin to environment by three technology(got-dip galvanizing,electrogalvanizing and mechanical galvanizing)was analyzed.
从环境保护的观点出发 ,分析了热浸镀锌、电镀锌和机械镀锌三种主要镀锌工艺对环境产生的影响与治理 ,认为机械镀锌对环境危害最小 ,热浸镀锌次之 ,电镀最严重 。
补充资料：机械镀
分子式：
CAS号：
性质：将冲击料(如玻璃球)、表面处理剂、镀覆促进剂、金属粉和镀件一起放入滚筒中，并通过滚筒滚动时产生的动能，把金属粉冷压到零件表面上形成镀层的过程。机械镀的镀层无氢脆，厚度均匀，但外观不如电镀层平滑、光亮。适于机械镀的金属有锌、镉、锡、铝、铜等软金属或它们的合金；适于机械镀的零件有螺钉、螺帽、垫片、铁钉、销钉、簧片等小零件及对氢脆敏感的高强钢与弹簧。
CAS号：
性质：将冲击料(如玻璃球)、表面处理剂、镀覆促进剂、金属粉和镀件一起放入滚筒中，并通过滚筒滚动时产生的动能，把金属粉冷压到零件表面上形成镀层的过程。机械镀的镀层无氢脆，厚度均匀，但外观不如电镀层平滑、光亮。适于机械镀的金属有锌、镉、锡、铝、铜等软金属或它们的合金；适于机械镀的零件有螺钉、螺帽、垫片、铁钉、销钉、簧片等小零件及对氢脆敏感的高强钢与弹簧。