1) edge cracks
裂边
1.
The hydrogen content and processing edge cracks was one of the important facts that effected the quality of 5005 aluminium alloy casting-rolling strips.
熔体质量和工艺裂边是影响5005合金铸轧产品质量的重要因素之一。
2.
The edge cracks of aluminum continuous cast-rolled strips result from that the cast-rolling zone is a little higher,the structure of tips is not reasonable,and the quality of cast-rolling roller is not good.
铝铸轧板坯产生严重裂边的主要原因是，铸轧区偏高、供料嘴结构不合理和铸轧辊质量不佳。
3.
The excellent aluminum casting-rolling strips mainly refer to those having good inherent organizational performance, the bright and clean surface and the free of the small edge cracks.
优质铝铸轧带材就是指具有优良的内部组织性能、光洁的表面质量以及较小裂边的带材。
2) cracked edge
裂边
1.
Too many existing cracked edge defects have appeared since the 1500-mm hot rolled wide strip went into operation in Laiwu Steel Group,Ltd.
莱钢1500mm热轧带钢生产线投产以来,出现了较多的裂边缺陷。
3) burst edge
裂边
1.
Through an analysis of chemical compositions,mechanical properties,metallographic structures,inclusions of Q345B wide strip steel,it was found that original cracks exist in casting blank and that while rolling,a great amount of inclusions and too high content of manganese lead to the further expansion of them,ultimately to form burst edges.
通过对Q345B裂边宽带钢化学成分、机械性能、金相组织、夹杂物的检验分析,发现是由于铸坯存在原始裂纹,轧制中大量夹杂物及过高锰含量导致裂纹的进一步扩展,最终形成裂边。
2.
This anticle analyzes edge crack on Q345B wide strip steel of chemical composition,me- chanical property,metallographical organization,metallic inclusion and find to he due to cast steel existing original flaw ,while rolling,great amount metallic inclusion and overtop Manganese con- tents to lead to flaw further expand,ultimate to form burst edg
通过对 Q345B 裂边宽带钢化学成分、机械性能、金相组织、夹杂物的检验分析,发现是由于铸坯存在原始裂纹,轧制中大量夹杂物及过高锰含量导致裂纹的进一步扩展,最终形成裂边。
4) edge cracking
边裂
1.
Structure testing in low magnification,microscopic test,spectrum test,chemical composition test and analysis about process controlling parameters were used to study the edge cracking of J55 strip steel coil of Ji- nan Iron and Steel Group,and then the measures for avoiding edge cracking were put forward,eventually gain dra- matic outcome.
针对济钢J55热轧钢带边裂问题,通过低倍组织检验、金相和光谱分析、化学成分试验等方法,分析了生产过程控制参数,研究了热轧钢带边裂的成因,提出了改进措施,并取得了显著效果。
2.
The mechanism and cause of edge cracking defect of hot-rolled strip in Kunming Iron & Steel co.
对昆钢热轧板卷边裂缺陷机理及成因进行了研究分析,提出了相应的预防控制措施,取得了较好的效果。
3.
The reasons and mechanism of edge cracking of austenite hot - rolled stainless strips are discussed.
对热轧奥氏体不锈带钢边裂产生的原因和形成机理进行了探讨。
5) edge crack
边裂
1.
Control and Analysis on Edge Crack of Hot Rolled Strip Coil Produced by CSP Process;
CSP工艺生产热轧板卷边裂的分析和控制
2.
Study on edge cracking and property characters of the corrosion resistant steel;
耐候钢带边裂问题及性能特性探讨
3.
In order to improve these indexes corresponding measures are put forward, mainly including reduction of edge crack of hot rolled coils and cold rolled high silicon products.
根据冷轧硅钢片成材率、板形质量和横向厚度精度现状,分析了这些指标的主要影响因素,提出了通过减少热轧卷边裂、冷轧高硅产品边裂以改善上述指标的措施。
6) edge cracks
边裂
1.
Control on slab edge cracks for Vanadium microalloying steel casting;
含钒微合金化钢铸坯边裂的控制
2.
It is proved that content of residual elements of steel, especially copper, is the key factor on causing edge cracks of hot-rolled light gauge strips by mass of data of production practice.
通过大量的生产试验与数据,证明了钢中残余元素特别是Cu含量是引起热轧薄板边裂的主要原因。