1) Sanitary ware
卫生陶瓷
1.
Application of additive in the slurry of sanitary ware;
卫生陶瓷泥浆添加剂的应用研究
2.
The super-smooth glaze of sanitary ware was obtained by once-fired technique.
采用一次烧成工艺制备了卫生陶瓷用超平滑釉(Ra≤10。
3.
The present developing status and standards of sanitary ware industry are summarized in this paper.
归纳了当今卫生陶瓷工业的发展现状和水平 ,对窑炉产业提出了的新要求 ,分析了某一新型窑炉的特点 ,对发展我国陶瓷窑炉产业提出了建
2) sanitary ceramics
卫生陶瓷
1.
Complexity of the gelcasting process for sanitary ceramics makes it difficult to control the dry shrinkage of the green body.
卫生陶瓷凝胶注模成型工艺的复杂性使其很难控制材料成型后的干燥收缩率,尝试用人工神经网络技术对卫生陶瓷凝胶注模成型工艺过程进行识别和仿真,采用Levenberg-Marquardt算法建立了卫生陶瓷凝胶注模成型工艺中单体、引发剂、交联剂、催化剂含量和坯体干燥收缩的映射网络模型,从而可利用该模型来预测在一定有机成型添加剂含量下卫生陶瓷的干燥收缩。
2.
Temperature and humidity in casting workshop for sanitary ceramics are very important for the quality of semi-finished product, but the traditional drying system is mostly independent.
卫生陶瓷成型车间的温度和湿度对半成品的成品率至关重要,其热源大都采用单独供应的办法,本文介绍了利用隧道窑余热对成型车间供热的情况。
3.
In order to controll the gelcasting process of sanitary ceramics by computer, a prediction model for the properties of shaped green sanitary ceramics body prepared by gelcasting based on BP artificial neural net is established.
为了实现对卫生陶瓷凝胶注模成型工艺的计算机控制,采用BP神经网络对获得的实验数据进行训练,建立了卫生陶瓷凝胶注模成型工艺参数和成型后坯体性能的映射网络模型,从而可利用该模型来预测在一定工艺条件下卫生陶瓷的性能。
3) sanitary wares
卫生陶瓷
1.
The applications of Guangxi-Qidao clay in ceramic paste and glaze of sanitary wares are studied on the basis of the study about the clay’s raw material capability.
在对广西气刀土原料性能研究的基础上,进行了在卫生陶瓷坯料、釉料中的应用研究。
2.
Through the adjust ion of Si/Al proportion and the doping of talc and matting agents,a calcium mat glaze for sanitary wares has been developed in this experiment.
本试验通过调整卫生陶瓷釉浆中的Si/Al,引入滑石和无光剂 ,成功地制备出卫生陶瓷钙质无光釉。
3.
The slip properties of the pressure casting on sanitary wares are studied,through a series of test,the influence of the slip properties of the slip casting process are discussed.
研究了卫生陶瓷压力注浆成型的泥浆性能 ,通过一系列试验 ,讨论了泥浆性能对压力注浆成型的影响。
4) sanitary ceramic
卫生陶瓷
1.
The effect of industrial wastes on the properties of ceramic slurry for sanitary ceramics was studied,and the optimum introduced quantity of the wastes was difined.
研究了一些工业废物对卫生陶瓷泥浆性能的影响 ,并确定了这些废物的最佳引入量。
2.
This paper describes what quality data should be collected from each procedure of sanitary ceramic manufacture,analyzes the importance of these data,and introduces application of these data through QC tools to improve and evaluate the procedure of products development in ceramic field.
阐述了卫生陶瓷各工艺过程需要采集的主要质量数据,分析说明了这些数据的重要性,同时介绍了如何应用QC工具加以分析利用这些数据,用以改善和评估卫生陶瓷新产品的研发试验过程。
3.
This article elaborated the production technology、quality control and measurement methods of gypsum powder used in sanitary ceramic working mold.
阐述了我国卫生陶瓷工作模用石膏粉的生产工艺、质量控制、检测方法等的现状;对我国具有代表性的石膏粉产品取样并进行了性能捡测、分析;研究了影响石膏粉质量和石膏模质量的主要因素:提出了建立卫生陶瓷工作模用石膏粉产品标准和检测标准的必要性。
5) sanitary
[英]['sænətri] [美]['sænə'tɛrɪ]
卫生陶瓷
1.
The cross experimental research of Gel-casting technology on sanitary by using hydroxymethylacrylamide(HMAM)as monomerand ceric ammonium nitrate as initiator,N,N,N',N'-tetramethylethylenedimaine as catalyst,N,N'-methylenebisacrylamide(MBAM)as cross-linkeris conducted.
本文采用正交实验方法,以羟甲基丙烯酰胺为单体,硝酸铈铵为引发剂,N,N,N',N'-四甲基乙二胺为催化剂,N,N'-亚甲基双丙烯酰胺为交联剂,研究了卫生陶瓷凝胶注模成型工艺,并探讨了不同工艺条件(单体加入量、引发剂加入量、催化剂加入量、交联剂加入量等因素)对卫生陶瓷料浆凝胶注模成形后坯体的干燥速率、收缩率、干燥强度以及综合性能指标的影响规律。
2.
Gelcasting technology of sanitary using acrylamide as monomer and (NH 4) 2S 2O 8-NaHSO 3 as redox initiator was studied.
采用凝胶注模成型方法 ,以丙烯酰胺为单体 ,( NH4 ) 2 S2 O8-Na HSO3为引发剂 ,研究了卫生陶瓷凝胶注模成型工艺。
6) construction ceramics
建筑卫生陶瓷
1.
Based on a SWOT analysis the author summarized the strategic choices available for theGuangdong construction ceramics enterprise in its cerrent state.
通过对佛山、东莞等地的陶瓷产区相关企业的调查研究,在SWOT分析的基础上,研究了相关的竞争战略,归纳总结出现阶段适合建筑卫生陶瓷企业的战略:即以低成本为竞争生存方式,差异性为竞争发展动力,国际化为发展长期最终目标。
2.
Due to the large amount of research required for this article, what's presented here is a summary of the current situation of construction ceramics in certain geographical locations, paying particular attention to the province of Guangdong.
文章通过大量的调查研究,概述了中国特别是广东省建筑卫生陶瓷企业的现状,采用SWOT分析方法,对该行业的企业所处的优势、劣势、面对的机遇和挑战进行了全面的研究分析,预测了建筑卫生陶瓷未来发展的总体趋势。
补充资料：卫生陶瓷
卫生间、厨房和试验室等场所用的带釉陶瓷制品，也称卫生洁具。按制品材质有熟料陶(吸水率小于18％)、精陶（吸水率小于12％）、 半瓷（吸水率小于5％）和瓷(吸水率小于0.5％)四种,其中以瓷制材料的性能为最好。熟料陶用于制造立式小便器、浴盆等大型器具，其余三种用于制造中、小型器具。各国的卫生陶瓷根据其使用环境条件，选用不同的材质制造。
中国生产的卫生陶瓷产品多属半瓷质和瓷质，有洗面器、大便器、小便器、妇洗器、水箱、洗涤槽、浴盆、返水管、肥皂盒、卫生纸盒、毛巾架、梳妆台板、挂衣钩、火车专用卫生器、化验槽等品类。每一品类又有许多形式,例如洗面器,有台式、墙挂式和立柱式等；大便器有坐式和蹲式，坐便器又按其排污方式有冲落式、虹吸式、喷射虹吸式、旋涡虹吸式等。
中国标准规定，各种半瓷质卫生陶瓷的吸水率小于或等于4.5％;耐急冷急热（100°C水中加热5分钟后投入15～16°C水中）三次不炸裂。普通釉白度大于或等于60度；白釉白度大于或等于70度。此外，对陶瓷的外观质量、规格、尺寸公差、使用功能等，也都有明确的规定。
卫生陶瓷的生产工艺，一般是在1250～1280°C温度条件下一次烧成。以高岭土（20～30％）、高塑性粘土(20～30％)、石英(30～40％)和钾长石(10～20％)为制坯主要原料，加入水和少量电解质，经磨细调制成规定性能的泥浆；以长石、 石英、石灰石、 白云石、滑石、菱镁石、氧化锌、碳酸钡为基础釉原料；以锆英石、氧化锡作白釉的乳浊剂；以铬锡红、铬绿、钒锆黄、钒锆蓝、镨锆黄、镨锆蓝等陶瓷颜料作色釉的着色原料。
卫生陶瓷因其形状复杂,普遍用石膏模浇注成型,中国一般采用架式管道压力注浆和真空回浆技术，其他国家有用台式注浆成型机、 传送带式注浆成型机、 洗面器立式注浆成型机等。对于形状和结构比较简单的产品，也有采用等静压和电泳成型方法。
烧成窑炉，中国多用重油烧的隔焰或半隔焰隧道窑，单层装烧；其他国家一般用天然气、煤油等洁净燃料烧的明焰隧道窑或棱式窑，单层或多层装烧。
80年代，卫生陶瓷产品都在进一步向提高使用功能、降低噪声、减轻重量、节约用水、安装方便、使用舒适、造型和装饰美观等方面发展。生产厂不仅向用户提供组装好的单件卫生器，而且提供配套齐全的整个卫生间。生产工艺正向快速成型、低温快烧及采用高效节能窑等方面发展。（见彩图）
中国生产的卫生陶瓷产品多属半瓷质和瓷质，有洗面器、大便器、小便器、妇洗器、水箱、洗涤槽、浴盆、返水管、肥皂盒、卫生纸盒、毛巾架、梳妆台板、挂衣钩、火车专用卫生器、化验槽等品类。每一品类又有许多形式,例如洗面器,有台式、墙挂式和立柱式等；大便器有坐式和蹲式，坐便器又按其排污方式有冲落式、虹吸式、喷射虹吸式、旋涡虹吸式等。
中国标准规定，各种半瓷质卫生陶瓷的吸水率小于或等于4.5％;耐急冷急热（100°C水中加热5分钟后投入15～16°C水中）三次不炸裂。普通釉白度大于或等于60度；白釉白度大于或等于70度。此外，对陶瓷的外观质量、规格、尺寸公差、使用功能等，也都有明确的规定。
卫生陶瓷的生产工艺，一般是在1250～1280°C温度条件下一次烧成。以高岭土（20～30％）、高塑性粘土(20～30％)、石英(30～40％)和钾长石(10～20％)为制坯主要原料，加入水和少量电解质，经磨细调制成规定性能的泥浆；以长石、 石英、石灰石、 白云石、滑石、菱镁石、氧化锌、碳酸钡为基础釉原料；以锆英石、氧化锡作白釉的乳浊剂；以铬锡红、铬绿、钒锆黄、钒锆蓝、镨锆黄、镨锆蓝等陶瓷颜料作色釉的着色原料。
卫生陶瓷因其形状复杂,普遍用石膏模浇注成型,中国一般采用架式管道压力注浆和真空回浆技术，其他国家有用台式注浆成型机、 传送带式注浆成型机、 洗面器立式注浆成型机等。对于形状和结构比较简单的产品，也有采用等静压和电泳成型方法。
烧成窑炉，中国多用重油烧的隔焰或半隔焰隧道窑，单层装烧；其他国家一般用天然气、煤油等洁净燃料烧的明焰隧道窑或棱式窑，单层或多层装烧。
80年代，卫生陶瓷产品都在进一步向提高使用功能、降低噪声、减轻重量、节约用水、安装方便、使用舒适、造型和装饰美观等方面发展。生产厂不仅向用户提供组装好的单件卫生器，而且提供配套齐全的整个卫生间。生产工艺正向快速成型、低温快烧及采用高效节能窑等方面发展。（见彩图）