1) hot-rolled wave of web
热轧腹板浪
2) web-wave
腹板波浪
1.
The mechanism and conditions of web-wave formation during hot rolling of H-Beam were studied.
对H型钢轧制过程中腹板波浪的产生机理及形成条件进行了研究。
3) cooled wave of web
冷却腹板浪
4) hot rolled strip
热轧薄板
1.
In this paper,the mechanisms of formation of rolled-in scale and scale mark are analyzed which are the major surface defects of continuous hot rolled strip used for cold rolling.
针对供冷轧用热轧薄板表面出现的氧化铁皮麻点表面缺陷,介绍了氧化铁皮压入与氧化铁皮麻点形成的机理,并分析了该缺陷的成因,结合首钢迁钢2160热轧线实际生产经验,提出了预防和减少该缺陷的措施。
6) Hot Rolled Sheet
热轧薄板
1.
The microscope,SEM,EDS and so on are used to analysis the reasons of the edge cracks of the hot rolled sheet.
采用化学成分分析、金相检验、扫描电镜及能谱分析等方法对连铸连轧(CSP)工艺生产的热轧薄板出现边裂的原因进行了分析。