1) potassium siliofluoride precipitation
氟硅酸钾沉淀
2) potassium fluosilicate
氟硅酸钾
1.
The process of preparating potassium fluosilicate from the mother liquor of magnessium fluoride has been studied.
研究了以氟化镁母液为原料制取氟硅酸钾的工艺过程,通过试验获得了最佳工艺条件。
2.
In the wet-process phosphoric acid production from the Hubei phosphate ore, one of the bothersome problems is that potassium fluosilicate and sodium fluosilicate scales are liable to form on the filtration system owing to its high potassium and sodium content, which greatly restrains the application of Hubei phosphate ore.
本文首先采用人工冷却系统模拟湿法磷酸生产的真空过滤系统冷却过程，研究垢物的析出规律，实验结果得知：垢物的主要成分为氟硅酸钠和氟硅酸钾，氟硅酸钠首先析出，结构致密，其次是氟硅酸钾，最后是二水硫酸钙，氟硅酸钠对氟硅酸钾有很强的结晶诱导作用；然后在三种生产中常用的不同的材质钼二钛、聚氯乙烯和聚四氟乙烯表面进行结垢试验，发现聚四氟乙烯表面最不易结垢，而在钼二钛表面最易结垢。
3) potassium fluorosilicate
氟硅酸钾
1.
Thin layer soaking method is used to determine the contact angle of sodium fluorosilicate, potassium fluorosilicate, gypsum against phosphoric aicd.
利用薄层浸润法测定固液间的接触角 ,通过 L ifshitz Van der Waals界面能理论计算氟硅酸钠、氟硅酸钾及二水硫酸钙与磷酸的固液界面能 ,研究得知其大小顺序为 :氟硅酸钠 <氟硅酸钾 <二水硫酸钙 ,因此 ,在理论上最先析出氟硅酸钠 ,其次是氟硅酸钾 ,最后析出二水硫酸
2.
Based on the platform of Aspen Plus engineering software, the production process of anhydrous hydrogen fluoride (AHF) from potassium fluorosilicate and sulfuric acid was simulated and analyzed.
基于ASPENPLUS软件平台,对氟硅酸钾与硫酸反应制取无水氟化氢的工艺进行了模拟分析,根据氟硅酸钾与硫酸的反应条件及反应后混合气的分离条件,采用ELECNRTL物性方法及NRTL物性方法,确定出当反应条件选取0。
4) potassium (sodium) fluosilicate
氟硅酸钾(钠)
5) potassium hexafluorosilicate
六氟硅酸钾
6) the potassium pyroantimonate cytochemical method
焦锑酸钾沉淀法
补充资料：氟硅酸
化学式H2SiF6。为一种强酸。二水合氟硅酸为无色晶体,熔点约19°C。氟硅酸在水溶液中很稳定,氢氟酸的含量极微。13.3％浓度的溶液是共沸溶液，可以蒸馏而不改变溶液的浓度。在蒸气中，即使在室温下也有50％以上的氟硅酸分解为氢氟酸和四氟化硅。氟硅酸可由氢氟酸与四氟化硅化合而成：
2HF+SiF4─→H2SiF6通常是将四氟化硅气体通入水内，滤去生成的硅酸凝胶而制得：
3SiF4+4H2O─→2H2SiF6+H4SiO4氟硅酸可作杀菌剂。
2HF+SiF4─→H2SiF6通常是将四氟化硅气体通入水内，滤去生成的硅酸凝胶而制得：
3SiF4+4H2O─→2H2SiF6+H4SiO4氟硅酸可作杀菌剂。