1) aluminum and aluminum alloy
铝及铝合金
1.
Microstructure and strength of aluminum and aluminum alloy joint brazed with rapidly-cooled Al-Si-Cu-Zn filler metals;
Al-Si-Cu-Zn急冷钎料钎焊铝及铝合金的界面结构及强度
2.
Green bright dipping process for aluminum and aluminum alloy;
铝及铝合金环保出光工艺
3.
Study on the process of electroless Ni-P alloys plating on aluminum and aluminum alloy;
铝及铝合金化学镀Ni-P合金工艺研究
2) aluminum and its alloys
铝及铝合金
1.
An environmentally acceptable chemical conversion agent CF-5 was formulated from non-toxic titanium salt, zirconium slat, and organic polymer so as to replace the conventional toxic chromium(Ⅵ) passivation agent used for aluminum and its alloys.
开发了一种由无毒的钛盐、锆盐和有机聚合物组成的铝及铝合金化学转化剂CF-5,以取代有毒的六价铬钝化。
2.
The development of zincation for aluminum and its alloys, from using s imple concentrated solution to dilute solution, finally to multi-metal and cyanide s olution, is described in detail.
较详细地阐述了铝及铝合金浸锌工艺 ,从单纯的浸浓溶液到稀溶液 ,再到多元合金的浸锌溶液及无氰浸锌溶液的发展过程 ,分析了浸锌工艺的优点与缺点 ,及防止浸锌工艺引出的特殊腐蚀问题的措施 ,对浸锌机理进行了初步探索。
3.
This paper described the recently progress on surface treatment of aluminum and its alloys.
本文简要介绍了目前铝及铝合金表面处理技术的进展。
3) aluminum and its alloy
铝及铝合金
1.
Determination of fluoride ions in chromating bath of aluminum and its alloys;
铝及铝合金铬酸盐转化处理槽中氟离子的测定
2.
Research progress of chromate-free surface treatment technology on aluminum and its alloys
铝及铝合金无铬表面处理技术研究进展
3.
With chemical oxidizing and subsequently pai nt ing of aluminum and its alloy, adhesion of aluminum substrate with coatings cou l d be greatly improved, as well as corrosion resistance.
铝及铝合金化学氧化后涂漆,可大大提高基体与涂层的结合力,并增强铝材的抗蚀能力。
4) Aluminium and Aluminium alloy
铝及铝合金
1.
Determination of Fe, Cu, Si, Mn, Mg, Cr,Zn, Ti and Ga Elements in Aluminium and Aluminium Alloy on Import & Export;
进出口铝及铝合金中Fe、Cu、Si、Mn、Mg、Cr、Zn、Ti、Ga等元素的测定
2.
Chromating technology of aluminium and aluminium alloy are introduced.
对铝及铝合金的铬酸盐转化膜工艺作了介绍,论述了铬酸盐转化膜工艺的日常管理及注意事项。
3.
The EDTA-H 2O 2 specteophotometry method can determined iron in the aluminium and aluminium alloy.
在pH≥ 10 2的氨性介质中 ,Fe(Ⅲ )与EDTA及H2 O2 形成稳定的紫红色三元配合物 ,铁量在 0～ 0 0 6mg/ml范围内符合比耳定律 ,可用于铝及铝合金中铁的测
5) aluminum and aluminum alloys
铝及铝合金
1.
This paper sums up the research methods of melting structure and the process of research on melt structure of aluminum and aluminum alloys, and especially gives a detailed introduction to Al-TM-X和 Al-Si-X system alloys.
综述了最近几十年来液态结构研究方法、铝及铝合金熔体结构研究的进展,特别是对Al-TM(过渡族元素)-X和Al-Si-X合金系做了详细介绍,希望为研究更高质量的铝合金熔体,精确控制铝及铝合金中的相组成提供理论指导。
2.
The technological properties of laser welding for aluminum and aluminum alloys are described.
概述了以激光为热源的铝及铝合金激光焊接技术特性。
6) aluminium and aluminium alloy tube
铝及铝合金管
1.
Air hole, burnthrough, cooapse and welding crackle occurred in the fixed overhead weld for aluminium and aluminium alloy tubes, above all the small-size thin wall tube.
针对铝及铝合金管,特别是小口径薄壁管固定口仰焊部位易出现气孔、烧穿、塌陷及焊接热裂纹等问题,分析问题存在的原因,从焊接工艺方面入手,提出一套消除气孔及烧穿的操作手法。
补充资料：铝和铝合金电镀
分子式：
分子量：
CAS号：
性质：纯铝具有较好的耐蚀性，但机械强度差，一些铝合金机械强度虽高，却耐热性、耐磨性差、接触电阻大和装饰性不佳等缺点。为改善其表面状态，必须进行表面处理。例如铝件镀或银，可改善其导电性；铝件镀铬，可增加表面硬度和耐磨性，并获得良好的装饰外观；铝件镀锡合金，可提高焊接性和减磨性等。在铝上进行电镀必须采取特殊的前处理工艺。一般经浸锌处理，铝表面的氧化膜被锌代替，就可电镀其他金属。
分子量：
CAS号：
性质：纯铝具有较好的耐蚀性，但机械强度差，一些铝合金机械强度虽高，却耐热性、耐磨性差、接触电阻大和装饰性不佳等缺点。为改善其表面状态，必须进行表面处理。例如铝件镀或银，可改善其导电性；铝件镀铬，可增加表面硬度和耐磨性，并获得良好的装饰外观；铝件镀锡合金，可提高焊接性和减磨性等。在铝上进行电镀必须采取特殊的前处理工艺。一般经浸锌处理，铝表面的氧化膜被锌代替，就可电镀其他金属。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。