1) crack initiation
裂纹萌生
1.
Simulating the drill string s crack initiation and propagation which is based on ABAQUS;
基于ABAQUS模拟钻柱裂纹萌生和扩展
2.
It has been observed that one types of crack initiation mechanism at the edge of surface small hole are possible.
研究了压力容器用钢16MnR在低周疲劳下微孔(40~200μm)的裂纹萌生与扩展规律。
3.
The results show that the fatigue crack initiation is frequently associated with the slip bands and the carbides at the specimen surfaces.
研究了K40S钴基高温合金在700℃和900℃温度条件下由应变控制的高温低周疲劳行为,对疲劳断口形貌进行观察,结果表明:在高温低周疲劳加载条件下,K40S合金疲劳裂纹萌生机制为表面滑移带开裂与表面碳化物相界面开裂的综合作用;疲劳裂纹萌生与扩展方式为穿晶型,瞬断区呈现枝晶断裂特征;碳化物可作为障碍,阻碍疲劳裂纹的扩展,且为主要的二次裂纹策源地;K40S合金高温低周疲劳断裂为机械疲劳与高温环境氧化共同作用的结果。
2) crack initiation energy
裂纹萌生功
1.
Results showed that the impact energy reached its limit but crack initiation energy and growth energy transformed while the cont.
研究了加入一定量成核剂的聚丙烯材料的冲击断裂行为 ,通过在一般Charpy冲击实验中采用仪表示波系统测定了材料的载荷 -时间曲线 ,通过该曲线将冲击断裂过程分为裂纹萌生和裂纹扩展两阶段 ,并计算出了裂纹萌生功和裂纹扩展功。
5) crack initiation region
裂纹萌生区
1.
The fracture surface was divided into crack initiation region and crack propagation region.
PA6/SGF的缺口拉伸断面主要分为裂纹萌生区及裂纹扩展区,基体的塑性变形主要集中在裂纹萌生区,剧烈的塑性变形可使基体上出现明显的孔洞。
6) fatigue crack initiation
疲劳裂纹萌生
1.
Study on fatigue crack initiation and propagation of cast aluminum alloy A356;
A356铸造铝合金的疲劳裂纹萌生及短裂纹扩展研究
2.
Cyclic stress response behavior, fatigue crack initiation and propagation behavior and (corresponding) fracture characteristics of magnesium alloys under fatigue loading condition are summarized.
简要介绍了镁合金在疲劳加载条件下的循环应力响应行为、疲劳裂纹萌生与扩展行为以及疲劳断裂的微观特征,分析了镁合金的显微组织、冶金和表面状态等材料内在因素以及环境、温度等外部因素对镁合金的疲劳强度、疲劳寿命、疲劳裂纹扩展速率的影响规律,指出了机械抛光、喷丸处理、表面滚压等表面机械加工方法以及适当的热处理均可有效地提高镁合金的疲劳强度和疲劳寿命。
3.
It was found that the grain boundaries are the preferred sites for fatigue crack initiation in the fatigued bicrystals.
在滑移带撞击晶界的地方，特别是在几条粗滑移带共同撞击晶界的地方观察到许多疲劳微裂纹；并且发现与平行晶界双晶相比，垂直晶界双晶中极有利于疲劳裂纹沿晶界作早期扩展一种PSB－GB疲劳裂纹萌生机制可用来解释这些沿晶疲劳裂纹的形成。