1) bending test
弯曲测试
1.
The theory and method of bending test on nanobeam for the measurement of Young′s modulus based on atomic force microscope(AFM) are introduced.
阐述了基于原子力显微镜(AFM)的弯曲测试测量纳米梁杨氏模量的理论和方法。
2.
The theory and method of bending test on silicon nanobeam for the thickness measurement based on atomic force microscope(AFM) are introduced.
本文阐述了基于原子力显微镜(AFM)的弯曲测试测量纳米梁厚度的理论和方法,并界定了基于AFM的厚度测量方法的适用条件,对基于AFM的厚度测量的两个典型应用进行了介绍。
3.
The Young\'s modulus of silicon nano-beam on 〈100〉 direction was measured by bending test method using an atomic force microscope(AFM).
为研究纳米梁的力学特性,采用SOI晶圆制备了硅双端固支梁纳米梁,利用典型的原子力显微镜(AFM)弯曲测试方法测试了硅纳米梁〈100〉晶向的杨氏模量。
2) three-point bending test
三点弯曲测试
3) plug pin bending test
插销弯曲测试
4) bend fatigue testing
弯曲疲劳测试
5) bend test
弯曲试验
1.
The roasting test and bend test results .
烘烤试验及弯曲试验表明,该工艺结合力很好。
2.
This paper firstly expatiates the object and purpose of the bend test during the welding procedure qualification.
通过对焊接工艺评定中弯曲试验评定对象和目的的阐述 ,结合国内外的焊接工艺评定标准对弯曲试验的不同要求 ,对焊接接头弯曲试验的力学模型进行了数学分析 ,得出采用不同弯曲试验标准可以得到不同的评定结果。
3.
Through the comparison between the outdated and the lastest standards it is found that althongh the years for preparation of two standards are different,bath for equivalent to the international standard ISO 7438:1985 “metallic materials-bend test” the definite answer has not found out for some questions.
通过新旧标准对比 ,发现两个标准虽然年代不同 ,但均等放采用国际标准ISO 7438:1985金属材料—弯曲试验 ,其中某些问题尚找不出确切的答案。
6) curing sample
弯曲试件
补充资料：弯曲工艺的概念及弯曲件
1．弯曲工艺：是根据零件形状的需要，通过模具和压力机把毛坯弯成一定角度，一定形状工件的冲压工艺方法。
2．弯曲成形工艺在工业生产中的应用：应用相当广泛，如汽车上很多履盖件，小汽车的柜架构件，摩托车上把柄，脚支架，单车上的支架构件，把柄，小的如门扣，夹子（铁夹）等。
弯曲的基本原理：以V形板料弯曲件的弯曲变形为例进行说明。其过程为：
1． 凸模运动接触板料（毛坯）由于凸,凹模不同的接触点力作用而产生弯矩， 在弯矩作用下发生弹性变形，产生弯曲。
2． 随着凸模继续下行，毛坯与凹模表面逐渐靠近接触，使弯曲半径及弯曲力臂均随之减少，毛坯与凹模接触点由凹模两肩移到凹模两斜面上。（塑变开始阶段）。
3．随着凸模的继续下行，毛坯两端接触凸模斜面开始弯曲。（回弯曲阶段）。
4．压平阶段，随着凸凹模间的间隙不断变小，板料在凸凹模间被压平。
5． 校正阶段，当行程终了，对板料进行校正，使其圆角直边与凸模全部贴合而成所需的形状。
弯曲变形的特点： 弯曲变形的特点是：板料在弯曲变形区内的曲率发生变化，即
弯 曲半径发生变化。从弯曲断面可划分为三个区：拉伸区、压缩区和中性层。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。